Modelo: ULTEM™ PEI PolyEtherImide with 30% Glass reinforced
Marca: Ultem ™
Unidades de venta | : | Kilogram |
Tipo de paquete | : | Paquete de exportación |
ULTEM ™ 2300 PEI es una polietherimida de vidrio extruida del 30%. Es un polímero amorfo y de alto rendimiento con una resistencia excepcional de llama y calor. Se realiza continuamente a 340 ° F (171 ° C), lo que lo hace ideal para aplicaciones de alta resistencia/alta calor, y aquellos que requieren propiedades dieléctricas consistentes en un amplio rango de frecuencia. Es resistente a la hidrólisis, altamente resistente a las soluciones ácidas y capaz de resistir múltiples ciclos de autoclave. ULTEM ™ 2300 proporciona una mayor rigidez y una mejor estabilidad dimensional al tiempo que mantiene muchas de las características útiles de Ultem ™ sin relleno. Ultem ™ se mecaniza comúnmente en partes para dispositivos médicos reutilizables, instrumentación analítica, aisladores eléctricos/electrónicos y una variedad de componentes estructurales que requieren alta resistencia y rigidez a temperaturas elevadas.
Ultem ™ PEI polietherimida (PEI) Ingeniería de plástico Ultem Pei PEI Combina alta resistencia y rigidez a temperaturas elevadas con resistencia al calor a largo plazo. ULTEM ™ PEI ofrece una excelente estabilidad dimensional combinada con una amplia resistencia química. ULTEM ™ PEI también es inherentemente resistente a la llama y se genera humo bajo. Ultem ™ PEI reforzado con vidrio proporciona una rigidez y estabilidad dimensionales aún mayores, al tiempo que mantiene muchas de las características útiles de Basic Ultem ™ PEI. El refuerzo de vidrio produce un producto con una relación de resistencia / peso excepcional y una mayor resistencia a la tracción. Este grado de 30% reforzado con vidrio es el Ultem ™ más relleno común y está fácilmente disponible en stock en formularios de hoja y varilla.
Ultem ™ 2300 PEI Nature Pei Sheet es una extrusión de propiedades de polietherimida reforzadas con el 30%
Pei Ultem Sheet Rod -Grades
Ultem® 1000
Ultem® 2100
Ultem® 2200
Ultem® 2400
Ultem® 2300 Ultem PEI 1000 SHOED Structure aumenta su rigidez y mejora la estabilidad dimensional al tiempo que mantiene muchas de las caractorísticas útiles de Ultem sin relleno. Además, dado que es un material amorfo, se debe tener cuidado si se mecaniza con refrigerante. Si se usa, los refrigerantes no aromáticos deben usarse para evitar el loco.
Specification | Test | Value | Units |
Specific Gravity, 73°F | D792 | 1.51 | – |
Tensile Strength @ Yield, 73°F | D638 | 17,000 | psi |
Tensile Modulus of Elasticity, 73°F | D638 | 800,000 | psi |
Tensile Elongation (at break), 73°F | D638 | 3 | % |
Flexural Strength, 73°F | D790 | 27,000 | psi |
Flexural Modulus of Elasticity | D790 | 850,000 | psi |
Shear Strength, 73°F | D732 | psi | |
Compressive Strength – Ultimate | psi | ||
Compressive Strength at 2% Deformation | D695 | psi | |
Compressive Strength at 10% Deformation | D695 | 32,000 | psi |
Deformation Under Load | < 1 | % | |
Compressive Modulus of Elasticity, 73°F | D695 | 625,000 | |
Compressive Strength ⊥ to Laminate (Modulus) | psi | ||
Compressive Strength ⊥ to Laminate (Yield) | psi | ||
Compressive Strength ⊥ to Laminate (Ultimate) | psi | ||
Hardness, Durometer (Shore “D” scale) | D2240 | D86 | |
Hardness, Rockwell (Scale as noted) | D785 | M112 (R127) | Rockwell M |
Izod Impact, Notched @ 73°F | D256 Type A | 1 | ft.lbs/in. of notch |
Coefficient of Friction (Dry vs Steel) Static | PTM 55007 | ||
Coefficient of Friction (Dry vs Steel) Dynamic | PTM 55007 | ||
Maximum Static Bearing Load (P) | PTM 55007 | 1,000 | psi |
Maximum Unlubricated No Load Bearing Velocity (V) | PTM 55007 | ft/minute | |
Maximum Limiting PV (Unlubricated) | PTM 55007 | psi x ft/min. | |
Wear Factor “K” x 10-10 | PTM 55010 | Cubic in.-min/ft.lbs.hr | |
Sand Wheel Wear/Abrasion Test | 80 | UHMW=100 | |
Minimum Mating Surface Hardness | 30 | Rockwell (Brinnell) | |
Coefficient of Linear Thermal Expansion | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
Coefficient of Thermal Expansion // to Laminates | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
Coefficient of Thermal Expansion I to Laminates | E-831 (TMA) | 1.1 | in/in/°F x 10-5 |
Softening Point | 400 | °F | |
Heat Deflection Temperature 264 psi | D648 | 410 | °F |
Embrittlement Temperature | °F Min. | ||
Continuous Service Temperature in Air | 340 | °F Max. | |
Short Term Service Temperature | 360 | °F Max. | |
Tg-Glass Transition (Amorphous) | D3418 | 410 | °F |
Melting Point (Crystalline) Peak | D3418 | °F | |
Thermal Conductivity | F433 | 1.56 | BTU-in/(hr/ft2°F) |
Dielectric Strength Short Term | D149 | 770 | Volts/mil |
Surface Resistivity | D257 | >1013 | ohm/cm |
Volume Resistivity | D257 | ohm/cm | |
Dielectric Constant, 106 Hz | D150 | 3.7 | |
Dissipation Factor, 106 Hz | D150 | 0.0015 | |
Flammability @ 3.1mm(1/8 in.) UL94 | UL94 | V-0 | |
Arc Resistance | seconds | ||
Water Absorption, Immersion 24 Hours | D570 (2) | 0.18 | % |
Water Absorption, Immersion Saturation | D570 (2) | .9 | % |
Machinability Rating | 1 | 1=easy, 10=difficult | |
Rod Diameter Availability (Off the Shelf) | .50 | 6.0 | inches |
Sheet Thickness Availability (Off the Shelf) | .030 | 3.0 | inches |
Characteristics / Attributes | Superior Chemical Resistance / 340F Cont. Service Temp Excellent rigidity and stiffness. |
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.